Creation

SKC hi-tech&marketing은 차세대 광학필름과 고기능 소재, Color Filter Millbase를 개발/생산하여
디스플레이 소재 산업을 Leading하고 있습니다.

반사 Film

Direct LED용 반사필름
  • SY260&SY750 빛 산란과 함께 뛰어난 반사성을 가진 LCD backlight용 반사 필름입니다.
  • SY750은 높은 반사율을 가지고 있는 것이 특징으로 고 휘도 Application에 적합한 제품입니다.
Property Unit SY260 SY750 Measured
General Thickness 188 188 SKC HT&M Method
Mechanical Tensile Strength(MD/TD) Kg/㎟ 13.5/13.1 8.6/9.2 ASTM D 882
Elongation at Break(MD/TD) % 130.0/110.0 101.8/82.0 ASTM D 882
Optical Reflectance (@550nm) % 96.2 97.9 SKC HT&M Method
Light Transmission % 2.7 2.7 ASTM D 1003
Gloss 60º (Inside/Outside) degree 25/24 27/26 ASTM D 523
Thermal Heat Shrinkage(MD/TD) % 3.0/2.0 1.6/1.3 SKC HT&M Method(150℃×30 min)
Cross Sectional Image SEM

This Information is the best currently available on the subject. The results should, however, only be regarded as a general guide to material properties and not as a guarantee. Some of the properties can be changed as a result of supplier's efforts to improve the quality or production efficiency of the subject.

Edge LED용 반사필름
  • 코팅 반사 Film은 반사 Sheet 표면과 LGP 사이의 손상으로부터 도광판(LGP)를 보호하고 디스플레이 화면의 균일성을
    향상시킵니다.
  • 코팅 반사 Film은 훌륭한 빛 표면의 균일성 향상을 통해 뛰어난 빛 산란 효과를 보여줍니다.
Property Unit RL603LA RL703LA RL603GA Measured
General Thickness 210 210 210 SKC HT&M Method
Mechanical Tensile Strength(MD/TD) Kg/㎟ 13.5/13.1 8.6/9.2 13.5/13.1 ASTM D 882
Elongation at Break(MD/TD) % 130.0/110.0 101.8/82.0 130.0/110.0 ASTM D 882
Optical Reflectance (@550nm) % 96.2 97.9 96.2 SKC HT&M Method
Light Transmission % 2.7 2.7 1.5 ASTM D 1003
Gloss 60º (Coated Side) degree 40 40 10 ASTM D 523
Thermal Heat Shrinkage(MD/TD) % 3.0/2.0 1.6/1.3 3.0/2.0 SKC HT&M Method
(150℃×30 min)
Cross Sectional Image SEM

This Information is the best currently available on the subject. The results should, however, only be regarded as a general guide to material properties and not as a guarantee. Some of the properties can be changed as a result of supplier's efforts to improve the quality or production efficiency of the subject.